Silicone Clothing Label Logo Textile Label Use Liquid Silicone with Factory Price/Embossing Silicone for -Shirt

• Customization: Available
• Material: Organic Silicone
• Application: Textile
• Model NO.: tcs-1310c
• Certification: REACH, RoHS
• Transport Package: 20kg/Bucket
• Trademark: tinhu
• Origin: China
• HS Code: 3910000000
• Production Capacity: 100000kg

Product Description

This is the embossed silicone rubber with high strength and easy to use .Our product is eco-friendy product , can contact with skin.

Silicone Rubber For Apparel Label TCS-1310C

Features & Usage:
TCS-1310C is an additional liquid silicone rubber with two components. It showed up good characteristics, such as excellent weatherability, dimensional stability, high transparency, avirulent environmental protection, high-adhesive strength, heatproof temperature exceeds 250C. It is widely used in printing of textile.
Technical parameters:

Items		Data
Before curing	appearance(silicone/curing)	subtransparent/colorless viscous liquid
	viscosity(silicone/curing)/mPa.s	300000/500
Operation time(25ºC)/h		5
After curing	hardness/Shore A	43
	density/g.cm^-3	1.10
	Tensile strength/MPa	9.0
	elongation/%	450
	Tear strength/kN.m^-1	20
	Shrinkage/%	0.1

Usage:
1.Mixture: Mix up silicone TCS-1310C with curing agent according ratio 10:1. (If curing agent increased, the curing speed will get slower). Mixture can complete by hand or by equipment.

Package, storage & Notes:

1. Silicone package: 20KG/pail.   Curing gent: 2KG/tin
2. Keep it dry, ventilative and cool. To prevent the rain, sun exposure.
3. Avoid mixing curing agent of condensation silicone. Below also can influent curing effect, such as amine, sulfur compounds, phosphorus compound & melt salt. Avoiding moisture intrusion in using.
4. The products storage period about 1 year. Its fluidity can be recovered when intense agitation. We advised stir the silicone first then stir the silicone & curing agent mixture second. Expired products also can be used if passed re-inspection.
5. This products is a non-dangerous goods.

 

Applycation:

Printing on the back of the fabrics o get 3D embossed effect by heat mold after high frequency embossing machine .

Easy to release from the mold, high transparency, strong adhesion, excellent softness , no fall off after washing , no shape change.

There is no any color migration on PU/Rubber material.

The embossing pattern was lasting and natural on the leatherware which can save long printing effect.

 

Operation method:

The mix ratio is 10:1

Thinner adding ratio: 10-40%, depends on fabric and embossing process

Heating temperature:150-190 degree

Normally the upside mold with temperature about 190 degree will better and downside mold with tem 150 degree .

Heating time :8-15 seconds ,depends on the heating temperature.