| Customization: | Available |
|---|---|
| Material: | Organic Silicone |
| Application: | Textile |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Quantity(Kilograms) | 1 - 200 | >200 |
| Est. Time(days) | 3 | To be negotiated |
| Product name :liquid silicone rubber for Clothing label making |
| Item : TCS-1140T 10USD/KG |
| Details : |
| This series of products are double component and liquid silicone rubber. It has good weatherability, good dimensional stability, moderate hardness, good fluidity, high transparency, non-toxic environmental protection, good adhesive force with various textile fabrics, and heat-resistant can be over 250 degrees C. The non-toxic special silk printed silica gel is a new type of printing adhesive with high strength, high transparency, high tear, soft hand, strong adhesive force, small shrinkage, and 5 hours of operation time. The new type of material used by German technology Taiwan joint venture is widely used in stereoscopic brand, garment printing, and printing. High quality products of ribbon and silk screen printing. use method 1.The glue and curing agent are mixed by weight ratio of 10: 1 (the glue increases the curing agent's dosage to slow the curing rate), and the mixing can be used manually or with the mixing equipment. 2. defoaming: the mixed rubber should be defoaming before making a label or printing a trademark on the cloth. In a vacuum, the volume of the rubber can be increased by 4-5 times. Therefore, the defoaming container should be 4-5 times larger than the volume of the rubber. After a few minutes, the volume of the adhesive is restored to normal. When there is no bubble escape on the surface (about ten minutes), the defoaming end and a small amount of use can be carried out in a vacuum dryer. 3.. It is used for defoaming. The rubber can be injected into the mold by heating or molding. Packing, storage and transportation and matters needing attention: 1. in this series of silica gel series, 20kg/ iron pail and curing agent are packed in 2kg/ iron cans. 2.. The silicone mesh series should be stored in dry, ventilated and cool places to prevent rain and sun exposure. 3.. This silencer silica gel series should avoid contact with silicone rubber curing agent during operation. It is possible that the compounds are not cured with amine, sulphur, phosphorus compounds and some metal salts. Moisture intrusion should be avoided during use. 4.. The storage period of this screen is about one year, and its liquidity can be resumed under the action of shear force (strong stirring). It is recommended to use the mixture in the container before mixing, then add the curing agent and stir evenly. Overdue reinspection can still be used. 5. this series of silica gel series is a non dangerous product. |
|
Model
|
tcs-1140t
|
Elongation at break(%)
|
600 |
|
Color
|
Transparent
|
Tensile strength(MPa)
|
10 |
|
Viscosity(mPa.s)
|
50000 ±1000
|
Shrinkage(%)
|
0.1
|
|
Hardness(shore A)
|
40 |
Relative density(g/cm³)
|
1.08 ±0.02
|
|
Working time(25ºC)h
|
12
|
Mixing ratio(by weight)
|
10:1
|
|
Cure time(130ºC)s
|
40 |
Tear stength(kN/m)
|
17
|